通过哪些方法可以提高不锈钢长城网带 链条网带 金属网带的寿命
编辑:扬州泉达金属网带厂   发布时间:2017-01-17

Great Wall stainless steel mesh belt, metal mesh belt surface has a layer of oxide film, makes Great Wall stainless steel mesh belt has certain corrosion resistance, but we will find that in the process of use, due to the Great Wall stainless steel mesh belt lubricating points of lubricant decomposition, makes Great Wall stainless steel mesh belt of chromium element chromium carbide production, and the reaction of chromium and nitrogen in the air is also generated the chromium nitride, these two compounds are hard brittle, thereby reducing the service life of the Great Wall stainless steel mesh belt is reduced greatly.

Oxide film is the key to the Great Wall stainless steel mesh belt life guarantee, it can be said for the protection of the oxidation film can greatly improve the life of the Great Wall stainless steel mesh belt. Let's learn about the measures taken in view of the these two compounds.

1, in view of the lubricant of the phenomenon, we can be exposed to the air of the stainless steel mesh belt to Great Wall stainless steel mesh belt at high temperatures. As a result, it can maintain the wall stainless steel mesh belt surface oxidation film, so that you can guarantee the stability of the oxide film.

2, in order to avoid the reaction of chromium and nitrogen, we if the temperature to 1000 degrees above, it also creates an oxidizing Great Wall stainless steel mesh belt, to maintain the stability of the oxide film. Regular special nursing was carried out on the Great Wall stainless steel mesh belt, is an effective method to avoid this kind of combination reaction.

不锈钢长城网带、金属网带表面有一层氧化膜,使得不锈钢长城网带具有一定的耐腐蚀性,但是我们在使用过程中会发现,由于不锈钢长城网带润滑点的润滑剂分解,使得不锈钢长城网带中的铬元素生产碳化铬,而空气中的氮气也和铬发生反应生成了氮化铬,这两种化合物都是硬脆化合物,从而降低了不锈钢长城网带的寿命大大降低。

    氧化膜是不锈钢长城网带寿命保证的关键,可以这样说对氧化膜的保护可以使得不锈钢长城网带的寿命大大提高。下面我们就来了解一下针对这两种化合物产生所采取的措施。

    1,针对润滑剂的这种现象,我们可以将暴露在空气中的不锈钢长城网带提高至不锈钢网带在高温区的温度。这样一来,它就可以维持不锈钢长城网带表层氧化膜,这样就可以保证氧化膜的稳定度了。

    2,为了避免铬与氮的反应,我们如果将温度提升至1000度以上,这样也可以使不锈钢长城网带产生氧化性,从而保持氧化膜的稳定性。定期对不锈钢长城网带进行特殊护理,是有效避免这种化合反应的方法。